The effect of numerous reprocessing cycles on transport properties of isotactic polypropylene (iPP) films was studied and related to the change of molecular weight and molecular weight distribution occurring during the recycling. Sorption curves of dichloromethane vapor in different samples of iPP were analyzed at 25°C to investigate the effect of structure modifications on the sorption mode. Moreover, gas permeability measurements were performed to evaluate the influence of reprocessing on the gas transport properties. The results obtained were attributed to modifications in the molecular structure of the polymer, evidenced from gel permeation chromatography (GPC), and to a different morphology of the films, as results from X-ray diffractograms and dynamic-mechanical thermal analysis (DMTA).
Structural Modifications Induced by Recycling of Polypropylene
INCARNATO, Loredana;SCARFATO, Paola;GORRASI, Giuliana;VITTORIA, Vittoria;
1999-01-01
Abstract
The effect of numerous reprocessing cycles on transport properties of isotactic polypropylene (iPP) films was studied and related to the change of molecular weight and molecular weight distribution occurring during the recycling. Sorption curves of dichloromethane vapor in different samples of iPP were analyzed at 25°C to investigate the effect of structure modifications on the sorption mode. Moreover, gas permeability measurements were performed to evaluate the influence of reprocessing on the gas transport properties. The results obtained were attributed to modifications in the molecular structure of the polymer, evidenced from gel permeation chromatography (GPC), and to a different morphology of the films, as results from X-ray diffractograms and dynamic-mechanical thermal analysis (DMTA).I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.