A magnetic study of superconductor/ferromagnet bilayers was performed by hysteresis loops and temperature-dependent magnetization measurements. The superconductor/ferromagnet bilayers consist of a Nb film deposited on a Py film with weak perpendicular magnetic anisotropy. By comparing the temperature-dependent magnetization data obtained on samples with different ferromagnetic layer thickness, a decrease of the magnetic pinning with increasing thickness of the ferromagnetic layer has been found. This is confirmed by the reduction of the Nb film critical current density at low fields extracted by using the magnetic irreversibility of the hysteresis loops. The reduction of the pinning can be related to the increase of the stripe width in the ferromagnetic layer observed by magnetic force microscopy (MFM) measurements.

Magnetic pinning in a superconducting film by a ferromagnetic layer with stripe domains

MANCUSI, DAVIDE;DI GIORGIO, CINZIA;BOBBA, Fabrizio;SCARFATO, Alessandro;CUCOLO, Anna Maria;PACE, Sandro;POLICHETTI, Massimiliano
2014-01-01

Abstract

A magnetic study of superconductor/ferromagnet bilayers was performed by hysteresis loops and temperature-dependent magnetization measurements. The superconductor/ferromagnet bilayers consist of a Nb film deposited on a Py film with weak perpendicular magnetic anisotropy. By comparing the temperature-dependent magnetization data obtained on samples with different ferromagnetic layer thickness, a decrease of the magnetic pinning with increasing thickness of the ferromagnetic layer has been found. This is confirmed by the reduction of the Nb film critical current density at low fields extracted by using the magnetic irreversibility of the hysteresis loops. The reduction of the pinning can be related to the increase of the stripe width in the ferromagnetic layer observed by magnetic force microscopy (MFM) measurements.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11386/4520880
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 5
social impact