Friction and wear behavior of ultra-high molecular weight polyethylene (UHMWPE) sliding against AISI420C austenitic stainless steel and against TiAl6V4 alloy under dry and lubricated conditions were investigated with a reciprocating pin-on-flat tribometer for comparative purposes. The tests were conducted by varying frequency of the pin alternative motion and the applied normal load. For the tests in lubricated conditions a fluid containing a large amount of sodium hyaluronate has been chosen. By using an electronic precision balance the wear mass loss of the UHMWPE samples was evaluated accordingly. Friction is greatly reduced by the presence of UHMWPE and this is believed to be due to the formation of a lubricating film of UHMWPE in the contact zone. Furthermore, the experimental investigation shows that the AISI420C/UHMWPE gives, in dry conditions, better values in the wear rate and in the friction coefficient than the TiAl6V4/UHMWPE.

Experimental analysis of tribological behavior of UHMWPE against AISI420C and against TiAl6V4 alloy under dry and lubricated conditions

RUGGIERO, Alessandro;
2015-01-01

Abstract

Friction and wear behavior of ultra-high molecular weight polyethylene (UHMWPE) sliding against AISI420C austenitic stainless steel and against TiAl6V4 alloy under dry and lubricated conditions were investigated with a reciprocating pin-on-flat tribometer for comparative purposes. The tests were conducted by varying frequency of the pin alternative motion and the applied normal load. For the tests in lubricated conditions a fluid containing a large amount of sodium hyaluronate has been chosen. By using an electronic precision balance the wear mass loss of the UHMWPE samples was evaluated accordingly. Friction is greatly reduced by the presence of UHMWPE and this is believed to be due to the formation of a lubricating film of UHMWPE in the contact zone. Furthermore, the experimental investigation shows that the AISI420C/UHMWPE gives, in dry conditions, better values in the wear rate and in the friction coefficient than the TiAl6V4/UHMWPE.
File in questo prodotto:
File Dimensione Formato  
760 Ruggiero Pre-print.pdf

accesso aperto

Descrizione: 0301-679X/& 2015 Elsevier Ltd. All rights reserved. Link editore: http://dx.doi.org/10.1016/j.triboint.2015.06.005
Tipologia: Documento in Pre-print (manoscritto inviato all'editore, precedente alla peer review)
Licenza: Creative commons
Dimensione 335.67 kB
Formato Adobe PDF
335.67 kB Adobe PDF Visualizza/Apri
760 Ruggiero Definitivo.pdf

non disponibili

Tipologia: Versione editoriale (versione pubblicata con il layout dell'editore)
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 2.87 MB
Formato Adobe PDF
2.87 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11386/4646202
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 98
  • ???jsp.display-item.citation.isi??? 82
social impact