IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishSyndiotactic polypropylene (sPP) was cast-extruded with a laboratory single screw extruder, obtaining a crystalline and still highly transparent film. The structural studies showed that the film crystallized at room temperature in the disordered helical form I, containing a fraction of a mesophase with the chains in trans-planar conformation. X-ray patterns, taken either along the extrusion direction (MD) or along the orthogonal directions (TD and ND), indicated a low orientation of the c axis parallel to the machine direction (MD) and a partial orientation of the a axis along the transverse direction (TD). Mechanical properties performed in either direction showed a very similar behaviour, but a different strain at the breaking point. The mechanical parameters were derived in both directions.
| Titolo: | Cast-extruded syndiotactic polypropylene films: Preliminary structural and mechanical results | |
| Autori: | ||
| Data di pubblicazione: | 2002 | |
| Rivista: | ||
| Abstract: | Syndiotactic polypropylene (sPP) was cast-extruded with a laboratory single screw extruder, obtaining a crystalline and still highly transparent film. The structural studies showed that the film crystallized at room temperature in the disordered helical form I, containing a fraction of a mesophase with the chains in trans-planar conformation. X-ray patterns, taken either along the extrusion direction (MD) or along the orthogonal directions (TD and ND), indicated a low orientation of the c axis parallel to the machine direction (MD) and a partial orientation of the a axis along the transverse direction (TD). Mechanical properties performed in either direction showed a very similar behaviour, but a different strain at the breaking point. The mechanical parameters were derived in both directions. | |
| Handle: | http://hdl.handle.net/11386/1064178 | |
| Appare nelle tipologie: | 1.1.2 Articolo su rivista con ISSN |
File in questo prodotto:
Copyright © 2021