A new amorphous silicon waveguide is realized by use of amorphous silicon carbon as cladding material. The structure is characterized both experimentally and theoretically, and its application for optical interconnections in photonic integrated circuits on silicon motherboards is proposed. The fabrication process is based on low-temperature (220°C) plasma-enhanced chemical-vapor deposition and is compatible with standard microelectronic processes. Propagation losses of 1.8 dB/cm have been measured at the fiber-optic wavelength of 1.3 µm. A strong thermo-optic coefficient has been measured in this material at this wavelength and exploited for the realization of a light-intensity modulator based on a Fabry—Perot interferometer that is tunable by temperature.

a-Si waveguides and light modulators for integrated photonics realized by low-temperature plasma enhanced chemical vapour deposition.

RUBINO, Alfredo;
1996-01-01

Abstract

A new amorphous silicon waveguide is realized by use of amorphous silicon carbon as cladding material. The structure is characterized both experimentally and theoretically, and its application for optical interconnections in photonic integrated circuits on silicon motherboards is proposed. The fabrication process is based on low-temperature (220°C) plasma-enhanced chemical-vapor deposition and is compatible with standard microelectronic processes. Propagation losses of 1.8 dB/cm have been measured at the fiber-optic wavelength of 1.3 µm. A strong thermo-optic coefficient has been measured in this material at this wavelength and exploited for the realization of a light-intensity modulator based on a Fabry—Perot interferometer that is tunable by temperature.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11386/3174477
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 77
  • ???jsp.display-item.citation.isi??? ND
social impact