The blown extrusion of poly(lactic acid) presents several challenges mainly due to its poor elongation properties. This work deals on the possibility to enhance the processabiliy of PLA by film blowing by functionalizing the polymer with nanosilicates. In particular, two types of polylactic acid (PLA 4032D and PLA 4042D) and different types of filler, selected from montmorillonites (Cloisite 30B) and bentonites (Nanofil SE3010) families, were used to prepare the hybrid systems by using a twin-screw extruder. The interaction between the polymer and the clay was evaluated by FTIR analysis and correlated to the structure of the obtained nanocomposites in terms of clay dispersion. All the samples were then submitted to rheological measurements both in shear and elongational mode.
Effect of polymer/clay composition on processability of polylactide nanocomposites by film blowing
GAROFALO, EMILIA;D'ARIENZO, LUCIA;DI MAIO, Luciano;INCARNATO, Loredana
2015-01-01
Abstract
The blown extrusion of poly(lactic acid) presents several challenges mainly due to its poor elongation properties. This work deals on the possibility to enhance the processabiliy of PLA by film blowing by functionalizing the polymer with nanosilicates. In particular, two types of polylactic acid (PLA 4032D and PLA 4042D) and different types of filler, selected from montmorillonites (Cloisite 30B) and bentonites (Nanofil SE3010) families, were used to prepare the hybrid systems by using a twin-screw extruder. The interaction between the polymer and the clay was evaluated by FTIR analysis and correlated to the structure of the obtained nanocomposites in terms of clay dispersion. All the samples were then submitted to rheological measurements both in shear and elongational mode.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.