The electric transport properties of flexible and transparent conducting bilayers, realized by sputtering ultrathin gold nanometric layers on sodium–alginate free-standing films, were studied. The reported results cover a range of temperatures from 3 to 300 K. In the case of gold layer thicknesses larger than 5 nm, a typical metallic behavior was observed. Conversely, for a gold thickness of 4.5 nm, an unusual resistance temperature dependence was found. The dominant transport mechanism below 70 K was identified as a fluctuation-induced tunneling process. This indicates that the conductive region is not continuous but is formed by gold clusters embedded in the polymeric matrix. Above 70 K, instead, the data can be interpreted using a phenomenological model, which assumes an anomalous expansion of the conductive region upon decreasing the temperature, in the range from 300 to 200 K. The approach herein adopted, complemented with other characterizations, can provide useful information for the development of innovative and green optoelectronics.

Electric Transport in Gold-Covered Sodium–Alginate Free-Standing Foils

Barone C.
Writing – Original Draft Preparation
;
Pagano S.
Writing – Original Draft Preparation
2021-01-01

Abstract

The electric transport properties of flexible and transparent conducting bilayers, realized by sputtering ultrathin gold nanometric layers on sodium–alginate free-standing films, were studied. The reported results cover a range of temperatures from 3 to 300 K. In the case of gold layer thicknesses larger than 5 nm, a typical metallic behavior was observed. Conversely, for a gold thickness of 4.5 nm, an unusual resistance temperature dependence was found. The dominant transport mechanism below 70 K was identified as a fluctuation-induced tunneling process. This indicates that the conductive region is not continuous but is formed by gold clusters embedded in the polymeric matrix. Above 70 K, instead, the data can be interpreted using a phenomenological model, which assumes an anomalous expansion of the conductive region upon decreasing the temperature, in the range from 300 to 200 K. The approach herein adopted, complemented with other characterizations, can provide useful information for the development of innovative and green optoelectronics.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11386/4759567
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 2
  • Scopus 5
  • ???jsp.display-item.citation.isi??? 4
social impact