Binary transition metal oxides with encouraging electrocatalyst properties have been suggested as electrode materials for supercapacitors and methanol oxidation. Hence, in this work, a binary mixed metal oxide based on nickel and manganese (MnNi2O4) and its hybrid with reduced graphene oxide were synthesized by a one-step hydrothermal method. After physical and morphological characterization, the potential of these nanostructures was investigated for use as supercapacitor electrodes and methanol electro-oxidation. The results of the electrochemical analysis showed a substantial effect of adding rGO to the MnNi2O4. The MnNi2O4/rGO hybrid electrode supercapacitor exhibited good stability of 93% after 2000 consecutive CV cycles and specific capacitance of 631 F/g at the scan rate of 10 mV/s. Furthermore, the application of this hybrid nanomaterial in the methanol electro-oxidation reaction (MOR) indicated its appropriate electrochemical efficiency and stability in methanol oxidation. Our results show that MnNi2O4/rGO can be considered as a promising electrode material for energy applications.
Enhanced electrochemical performance of MnNi2O4/rGO nanocomposite as pseudocapacitor electrode material and methanol electro-oxidation catalyst
Di Bartolomeo, Antonio
Writing – Review & Editing
;
2021-01-01
Abstract
Binary transition metal oxides with encouraging electrocatalyst properties have been suggested as electrode materials for supercapacitors and methanol oxidation. Hence, in this work, a binary mixed metal oxide based on nickel and manganese (MnNi2O4) and its hybrid with reduced graphene oxide were synthesized by a one-step hydrothermal method. After physical and morphological characterization, the potential of these nanostructures was investigated for use as supercapacitor electrodes and methanol electro-oxidation. The results of the electrochemical analysis showed a substantial effect of adding rGO to the MnNi2O4. The MnNi2O4/rGO hybrid electrode supercapacitor exhibited good stability of 93% after 2000 consecutive CV cycles and specific capacitance of 631 F/g at the scan rate of 10 mV/s. Furthermore, the application of this hybrid nanomaterial in the methanol electro-oxidation reaction (MOR) indicated its appropriate electrochemical efficiency and stability in methanol oxidation. Our results show that MnNi2O4/rGO can be considered as a promising electrode material for energy applications.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.