The aim of the paper is to compare a tensile strength and an elongation at break of the sandwich materials with different cores created with the polymeric composite mixture at simultaneous acting of the cyclic degradation. The sheet S235J0 is the face. The core of the sandwich panel is from the structural two-component adhesive, from the composite material based on the microparticles of the glass-bead, the rubber and the textile microfibre waste from the tyre recyclation and the rubber particle waste from the tyre recyclation. Namely the secondary raw materials based on the textile microfibres are difficult to utilize in another processing. This research showed one of prospective possibilities of the material utilization of this secondary raw material. The highest tensile strength of the sandwich materials is reached with the core from the composite material on the glass-bead base. The significant fall of the tensile strength of the sandwich materials was measured at the material with the core based on the rubber and textile microfibre waste from the tyre recyclation. The elongation at break was not almost changed. The core crackled at lower loading at first. The face tolerated higher loading.

Mechanical Characterisation of Metal/Polymeric Composite Waste/Metal Sandwich Panel

Muller M.;Ruggiero A.;
2017-01-01

Abstract

The aim of the paper is to compare a tensile strength and an elongation at break of the sandwich materials with different cores created with the polymeric composite mixture at simultaneous acting of the cyclic degradation. The sheet S235J0 is the face. The core of the sandwich panel is from the structural two-component adhesive, from the composite material based on the microparticles of the glass-bead, the rubber and the textile microfibre waste from the tyre recyclation and the rubber particle waste from the tyre recyclation. Namely the secondary raw materials based on the textile microfibres are difficult to utilize in another processing. This research showed one of prospective possibilities of the material utilization of this secondary raw material. The highest tensile strength of the sandwich materials is reached with the core from the composite material on the glass-bead base. The significant fall of the tensile strength of the sandwich materials was measured at the material with the core based on the rubber and textile microfibre waste from the tyre recyclation. The elongation at break was not almost changed. The core crackled at lower loading at first. The face tolerated higher loading.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11386/4865252
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 1
  • ???jsp.display-item.citation.isi??? ND
social impact