We present the fabrication of FeSe0.5Te0.5 polycrystalline samples by self-flux method, showing the presence of the peak-effect in the vortex lattice configuration. To improve the performances at high magnetic fields for this iron-based superconductor of the 11-family, the two-step solid-state reaction process has been successfully modified by increasing the temperature of the heat treatment and by slowing down the cooling rate. The magnetic field-temperature phase diagram has been investigated by magneto-resistance, magnetization, and heat capacity measurements in applied magnetic fields up to 18 T. The magnetization curves exhibit an enhancement of the peak-effect whose position shifts by varying the temperature, following a similar dependence than that previously reported in high-temperature superconducting materials such as YBa2Cu3O7-d. The presence of the peak-effect can be correlated to the sample manufacture, since by tuning a proper heat treatment it becomes observable ever more in the magnetic field-temperature phase diagram. This fabrication route paves the way to a systematic increase in the critical current density thus becoming relevant for applications.
Improvements of high-field pinning properties of polycrystalline Fe(Se,Te) material by heat treatments
Fiamozzi Zignani, C.;Leo, A.;Guarino, A.;Galluzzi, A.;Nigro, A.;Polichetti, M.;Pace, S.;
2019-01-01
Abstract
We present the fabrication of FeSe0.5Te0.5 polycrystalline samples by self-flux method, showing the presence of the peak-effect in the vortex lattice configuration. To improve the performances at high magnetic fields for this iron-based superconductor of the 11-family, the two-step solid-state reaction process has been successfully modified by increasing the temperature of the heat treatment and by slowing down the cooling rate. The magnetic field-temperature phase diagram has been investigated by magneto-resistance, magnetization, and heat capacity measurements in applied magnetic fields up to 18 T. The magnetization curves exhibit an enhancement of the peak-effect whose position shifts by varying the temperature, following a similar dependence than that previously reported in high-temperature superconducting materials such as YBa2Cu3O7-d. The presence of the peak-effect can be correlated to the sample manufacture, since by tuning a proper heat treatment it becomes observable ever more in the magnetic field-temperature phase diagram. This fabrication route paves the way to a systematic increase in the critical current density thus becoming relevant for applications.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.