Background The contour method for residual stress measurement has seen significant development, but an experimental reproducibility study utilizing physical samples has not been published. Objective A double-blind reproducibly study is reported, having scope beginning with EDM cutting and ending with residual stress calculation. Methods A reinforced I-beam sample geometry is identified for its unique residual stress profile when extracted from residual stress bearing quenched aluminum bar (7050-T74). Contour measurements are prescribed on a midplane of symmetry with dimensions 24.0 mm by 50.0 mm. Fourteen identically prepared samples are fabricated from a single long bar with well characterized and uniform residual stress. Five samples throughout the bar are identified for planning measurements to validate sample uniformity and overall suitability of the residual stress field. The planning measurements employ a range of techniques: contour method, neutron diffraction, and hole-drilling. Eight samples are distributed to an international group of participants to execute their standard measurement practice. A double-blind process is followed to provide anonymity. Results Results are provided by eight participants: six being self-similar and two being quite different, the latter set aside as outliers. An average residual stress field is established from non-outlying results and the spatial distribution of reproducibility standard deviation is determined. The average stress field ranges from -60 to 70 MPa and the reproducibility standard deviation averages 8.1 MPa on the measurement plane. The average reproducibility standard deviation is about 3 × larger for points within 1.0 mm of plane boundaries (17.6 MPa) than for the remaining points (6.1 MPa). Conclusions Reproducibility standard deviation (among different labs) for contour method residual stress measurement is found to be very similar to repeatability standard deviation (in a single lab) reported in prior work. The reproducibility observed here, for the entire measurement process, is also similar to that found in a prior reproducibility study limited to contour method data analysis.
Interlaboratory Reproducibility of Contour Method Data in a High Strength Aluminum Alloy
P. Carlone;F. Tucci;
2022-01-01
Abstract
Background The contour method for residual stress measurement has seen significant development, but an experimental reproducibility study utilizing physical samples has not been published. Objective A double-blind reproducibly study is reported, having scope beginning with EDM cutting and ending with residual stress calculation. Methods A reinforced I-beam sample geometry is identified for its unique residual stress profile when extracted from residual stress bearing quenched aluminum bar (7050-T74). Contour measurements are prescribed on a midplane of symmetry with dimensions 24.0 mm by 50.0 mm. Fourteen identically prepared samples are fabricated from a single long bar with well characterized and uniform residual stress. Five samples throughout the bar are identified for planning measurements to validate sample uniformity and overall suitability of the residual stress field. The planning measurements employ a range of techniques: contour method, neutron diffraction, and hole-drilling. Eight samples are distributed to an international group of participants to execute their standard measurement practice. A double-blind process is followed to provide anonymity. Results Results are provided by eight participants: six being self-similar and two being quite different, the latter set aside as outliers. An average residual stress field is established from non-outlying results and the spatial distribution of reproducibility standard deviation is determined. The average stress field ranges from -60 to 70 MPa and the reproducibility standard deviation averages 8.1 MPa on the measurement plane. The average reproducibility standard deviation is about 3 × larger for points within 1.0 mm of plane boundaries (17.6 MPa) than for the remaining points (6.1 MPa). Conclusions Reproducibility standard deviation (among different labs) for contour method residual stress measurement is found to be very similar to repeatability standard deviation (in a single lab) reported in prior work. The reproducibility observed here, for the entire measurement process, is also similar to that found in a prior reproducibility study limited to contour method data analysis.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.